有人用castep对LiFePO4做过结构优化和能带计算吗？

sophiazbs

    对LiFePO4进行了多次结构优化和能带计算，但是总是会出现下面的提示，请有经验的帮忙看下是什么问题？输出的castep文件见附件。

*Warning* max. SCF cycles performed but system has not reached the groundstate.

Current total energy, E     =  -12191.08891072     eV
Current free energy (E-TS)  =  -12191.08891072     eV
(energies not corrected for finite basis set)

NB est. 0K energy (E-0.5TS)      =  -12191.08891072     eV

  ********************************************************
  Warning: electronic minimisation did not converge during
           finite basis set correction.
  ********************************************************

jiangning198511

电子步没有收敛，加大步数

sophiazbs

jiangning198511 发表于 2017-2-28 13:31
电子步没有收敛，加大步数

你是说scf cycle max.的值吗？ 我从100调到200，还是不行

sophiazbs

jiangning198511 发表于 2017-2-28 13:31
电子步没有收敛，加大步数

Warning: electronic minimisation did not converge during
           finite basis set correction.
这里还有个提示

jiangning198511

sophiazbs 发表于 2017-2-28 16:19
Warning: electronic minimisation did not converge during
           finite basis set correction.
...

就是电子步没有收敛，看看有没有调节电子收敛的关键词，这个软件我也没咋用过

卡开发发

sophiazbs 发表于 2017-2-28 16:18
你是说scf cycle max.的值吗？ 我从100调到200，还是不行

electronic minimisation did not converge during finite basis set correction这个东西不是个提示，你可以当做报错，核心问题就是SCF没收敛。

先确保结构和磁序的初猜是正确的，其次是计算的参数，比如截断能是否充分等，如果再不能收敛就调整density mixing。

sophiazbs

卡开发发 发表于 2017-2-28 19:36
electronic minimisation did not converge during finite basis set correction这个东西不是个提示，你 ...

恩  谢谢   density mixing 调整 下应该还是可行的。我试试